Strong Match — 98.5% match
based on chemical composition and mechanical property overlap.
EN 10083-1 3C35 (EN 10083-1:1991) and EN 10083-2 C35 (EN 10083-2:2006) are both steel grades.
Both fall under the Carbon Steel category.
EN 10083-1 3C35 is typically used for quenched and tempered machine parts; non alloy steels also normalized (clause 1), while EN 10083-2 C35 is commonly used for crankshafts, axles, connecting rods, machine parts.
EN 10083-1 3C35 is defined under European Standard (EN), originating from Europe, while EN 10083-2 C35 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10083-1 3C35 vs EN 10083-2 C35 is a 97.8% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 98.5%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-1 3C35
EN 10083-2 C35
Condition
Quenched and tempered, ruling section d <= 16 mm
Quenched and tempered (+QT), ruling section d <= 16 mm
Elongation
17% min
17% min
Tensile Strength
630 to 780 MPa
630 to 780 MPa
Yield Strength
430 MPa min
430 MPa min
Typical Applications
EN 10083-1 3C35
Quenched and tempered machine parts; non alloy steels also normalized (clause 1)
EN 10083-2 C35
Crankshafts, axles, connecting rods, machine parts
Can EN 10083-1 3C35 Be Substituted With EN 10083-2 C35?
EN 10083-1 3C35 and EN 10083-2 C35 overlap closely enough on chemistry and mechanical properties that EN 10083-2 C35 is often considered as a substitute for EN 10083-1 3C35 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10083-1 3C35 and EN 10083-2 C35?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10083-1 3C35 be substituted with EN 10083-2 C35?
EN 10083-1 3C35 and EN 10083-2 C35 overlap closely enough on chemistry and mechanical properties that EN 10083-2 C35 is often considered as a substitute for EN 10083-1 3C35 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.