Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10083-1 51CrV4 (EN 10083-1:1991) and IS 3195 113C6 (IS 3195:1992) are both steel grades.
Both fall under the Spring Steel category.
EN 10083-1 51CrV4 is typically used for quenched and tempered machine parts; non alloy steels also normalized (clause 1), while IS 3195 113C6 is commonly used for volute and helical springs for railway rolling stock; flats and rounds, springs worked hot and heat-treated (clause 1.1, foreword).
EN 10083-1 51CrV4 is defined under European Standard (EN), originating from Europe, while IS 3195 113C6 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10083-1 51CrV4 vs IS 3195 113C6 is a 67.3% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-1 51CrV4
IS 3195 113C6
Condition
Quenched and tempered, ruling section d <= 16 mm
Not specified
Elongation
9% min
Not specified
Hardness
Soft annealed: 248 HB max
Not specified
Tensile Strength
1100 to 1300 MPa
Not specified
Yield Strength
900 MPa min
Not specified
Hardness, annealed
Not specified
<=240 HB
Typical Applications
EN 10083-1 51CrV4
Quenched and tempered machine parts; non alloy steels also normalized (clause 1)
IS 3195 113C6
Volute and helical springs for railway rolling stock; flats and rounds, springs worked hot and heat-treated (clause 1.1, foreword)
Key Differences
EN 10083-1 51CrV4 specifies Cr, V which are not specified for IS 3195 113C6.
Can EN 10083-1 51CrV4 Be Substituted With IS 3195 113C6?
EN 10083-1 51CrV4 and IS 3195 113C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-1 51CrV4 and IS 3195 113C6?
EN 10083-1 51CrV4 specifies Cr, V which are not specified for IS 3195 113C6.
Can EN 10083-1 51CrV4 be substituted with IS 3195 113C6?
EN 10083-1 51CrV4 and IS 3195 113C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.