Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10083-1 46CrS2 (EN 10083-1:1996) and IS 1570 (Part 7) 10Mo6H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Alloy Steel category.
EN 10083-1 46CrS2 is typically used for quenched and tempered machine parts (clause 1.1), while IS 1570 (Part 7) 10Mo6H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
EN 10083-1 46CrS2 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 10Mo6H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10083-1 46CrS2 vs IS 1570 (Part 7) 10Mo6H is a 61.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-1 46CrS2
IS 1570 (Part 7) 10Mo6H
Condition
Quenched and tempered, ruling section d <= 16 mm
Tubes, N+T, thickness - (first row of Table 3)
Elongation
12% min
>=30%
Hardness
Soft annealed: 223 HB max
Not specified
Tensile Strength
900 to 1100 MPa
>=415 MPa
Yield Strength
650 MPa min
>=205 MPa (0.2 % proof stress)
Typical Applications
EN 10083-1 46CrS2
Quenched and tempered machine parts (clause 1.1)
IS 1570 (Part 7) 10Mo6H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
IS 1570 (Part 7) 10Mo6H specifies Mo which is not specified for EN 10083-1 46CrS2.
Can EN 10083-1 46CrS2 Be Substituted With IS 1570 (Part 7) 10Mo6H?
EN 10083-1 46CrS2 and IS 1570 (Part 7) 10Mo6H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-1 46CrS2 and IS 1570 (Part 7) 10Mo6H?
IS 1570 (Part 7) 10Mo6H specifies Mo which is not specified for EN 10083-1 46CrS2.
Can EN 10083-1 46CrS2 be substituted with IS 1570 (Part 7) 10Mo6H?
EN 10083-1 46CrS2 and IS 1570 (Part 7) 10Mo6H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.