Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10083-1 C22R (EN 10083-1:1996) and BS 970 (Part 1) 060A72 (BS 970 (Part 1):1991) are both steel grades.
Both fall under the Carbon Steel category.
EN 10083-1 C22R is typically used for quenched and tempered machine parts; also used normalized (clause 1.1, table 10), while BS 970 (Part 1) 060A72 is commonly used for as-rolled, or as-rolled and softened, steel (section two).
EN 10083-1 C22R is defined under European Standard (EN), originating from Europe, while BS 970 (Part 1) 060A72 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, EN 10083-1 C22R vs BS 970 (Part 1) 060A72 is a 62.7% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-1 C22R
BS 970 (Part 1) 060A72
Condition
Quenched and tempered, ruling section d <= 16 mm
Not specified
Elongation
20% min
Not specified
Tensile Strength
500 to 650 MPa
Not specified
Yield Strength
340 MPa min
Not specified
Typical Applications
EN 10083-1 C22R
Quenched and tempered machine parts; also used normalized (clause 1.1, Table 10)
BS 970 (Part 1) 060A72
As-rolled, or as-rolled and softened, steel (section two)
Key Differences
EN 10083-1 C22R specifies Cr, Cr+Mo+Ni, Mo, Ni which are not specified for BS 970 (Part 1) 060A72.
Can EN 10083-1 C22R Be Substituted With BS 970 (Part 1) 060A72?
EN 10083-1 C22R and BS 970 (Part 1) 060A72 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-1 C22R and BS 970 (Part 1) 060A72?
EN 10083-1 C22R specifies Cr, Cr+Mo+Ni, Mo, Ni which are not specified for BS 970 (Part 1) 060A72.
Can EN 10083-1 C22R be substituted with BS 970 (Part 1) 060A72?
EN 10083-1 C22R and BS 970 (Part 1) 060A72 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.