EN 10083-1:1996 C25E Steel: Specifications & Listings
EN 10083-1:1996 C25E: A low carbon special steel for quenching and tempering to EN 10083-1:1991 + A1:1996 (steel number 1.1158), with sulphur max. 0.035%. Supplied as semi-finished products, bars, rod, wide flats, sheet, plate and strip, and forgings (clause 1.1). Quenched and tempered tensile strength 550 to 700 MPa for ruling sections up to 16 mm.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Cr
Cr+Mo+Ni
Mn
Mo
Ni
P
S
Si
0.22-0.29
<=0.40
<=0.63
0.40-0.70
<=0.10
<=0.40
<=0.035
<=0.035
<=0.40
Mechanical Properties
Condition
Quenched and tempered, ruling section d <= 16 mm
Elongation
19% min
Tensile Strength
550 to 700 MPa
Yield Strength
370 MPa min
More data from EN 10083-1:1996
From the standard
Other composition limitsTable 3 and its notes
Designation as printed
C25E
Steel number
1.1158
Pair grade
C25R has the same limits except sulphur, controlled 0.020 to 0.040
Availability
Printed in brackets: introduced for the first time in this standard and not available from stock in all countries (Table 3, note 6)
Improved machinability
Steels with lead or higher sulphur, up to about 0.100% S, may be supplied on request (Table 3, note 3)
Restricted options
Without hardenability or quenched and tempered or normalized property requirements, the carbon range may be restricted to 0.05% and/or the sum Cr + Mo + Ni to max. 0.45% by agreement (Table 3, note 5)
Elements not quoted in Table 3 are not intentionally added without the purchaser's agreement, other than for finishing the heat. With hardenability requirements, slight deviations within Table 4 are permitted except for carbon, phosphorus and sulphur.
Source: EN 10083-1:1991 + A1:1996 (DIN EN 10083-1:1996-10), Table 3 and its notes
Mechanical properties, quenched and tempered2 sections
Ruling section
Yield strength Re, min (MPa)
Tensile strength Rm (MPa)
Elongation A, min (%)
Reduction of area Z, min (%)
Impact KV, min (J)
d <= 16 mm, t <= 8 mm
370
550 to 700
19
45
45
16 mm < d <= 40 mm, 8 mm < t <= 20 mm
320
500 to 650
21
50
45
Re is the upper yield strength or, if no yield phenomenon occurs, the 0.2% proof strength; A on gauge length 5.65 times the root of the original cross section; KV on longitudinal Charpy V-notch test pieces, average of 3 values, no single value below 70% of the minimum average value. Ruling sections as in Annex A. Sizes not listed are not covered by the standard.
Source: EN 10083-1:1991 + A1:1996 (DIN EN 10083-1:1996-10), Table 9
Mechanical properties, normalized2 sizes
Size
Yield strength Re, min (MPa)
Tensile strength Rm, min (MPa)
Elongation A, min (%)
d <= 16 mm, t <= 16 mm
260
470
22
16 mm < d <= 100 mm, 16 mm < t <= 100 mm
230
440
23
Values also apply to the grades with hardenability requirements (+H, +HH, +HL). Sizes not listed are not covered by the standard.
Source: EN 10083-1:1991 + A1:1996 (DIN EN 10083-1:1996-10), Table 10
Maximum hardness by delivery conditionTable 8
Shearability
Shearable in the untreated condition under suitable conditions (clause 5.3.2.3)
Values also apply to the grades with hardenability requirements (+H, +HH, +HL); not applicable to continuously cast slabs not further worked.
Source: EN 10083-1:1991 + A1:1996 (DIN EN 10083-1:1996-10), Table 8
Heat treatmentTable 12
Quenching
860 to 900 deg C
Quenching agent
Water
Tempering
550 to 660 deg C
Normalizing
880 to 920 deg C
Guidance values except the end quench test temperature, which is binding. Lower quenching temperatures generally for water, upper for oil; austenitizing at least 30 min, tempering at least 60 min (guide values).
Source: EN 10083-1:1991 + A1:1996 (DIN EN 10083-1:1996-10), Table 12