EN 10083-2 C35E vs IS 1570 (Part 4) 10Mo6

Related Material — 65% match based on chemical composition and mechanical property overlap.

EN 10083-2 C35E (EN 10083-2:2006) and IS 1570 (Part 4) 10Mo6 (IS 1570 (Part 4):1988) are both steel grades. EN 10083-2 C35E is classified under Carbon Steel, while IS 1570 (Part 4) 10Mo6 is classified under Alloy Steel — a different category, which is worth noting alongside the chemistry match below. EN 10083-2 C35E is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 4) 10Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10083-2 C35E vs IS 1570 (Part 4) 10Mo6 is a 68.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With EN 10083-2 C35E:
BS 970 (Part 1) 040A04 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A67 BS 970 (Part 1) 040A12 BS 970 (Part 1) 060A62 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15
Match Breakdown
CHEMISTRY MATCH
68.4%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property EN 10083-2 C35E IS 1570 (Part 4) 10Mo6
Standard EN 10083-2:2006 IS 1570 (Part 4):1988
Category Carbon Steel Alloy Steel
C (%) 0.32-0.39 <=0.15
Cr (%) <=0.40 <=0.25
Cr+Mo+Ni (%) <=0.63 Not specified
Mn (%) 0.50-0.80 0.40-0.70
Mo (%) <=0.10 0.45-0.65
Ni (%) <=0.40 <=0.30
P (%) <=0.030 Not specified
S (%) <=0.035 Not specified
Si (%) <=0.40 0.15-0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10083-2 C35E IS 1570 (Part 4) 10Mo6
Condition Quenched and tempered (+QT), ruling section d <= 16 mm Not specified
Elongation 17% min Not specified
Tensile Strength 630 to 780 MPa Not specified
Yield Strength 430 MPa min Not specified
Typical Applications
EN 10083-2 C35E
Quenched and tempered, flame or induction hardened machine parts; can also be used normalized (clause 1)
IS 1570 (Part 4) 10Mo6
Not documented
Key Differences
Can EN 10083-2 C35E Be Substituted With IS 1570 (Part 4) 10Mo6?
EN 10083-2 C35E and IS 1570 (Part 4) 10Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10083-2 C35E
0 active listings and RFQs →
IS 1570 (Part 4) 10Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10083-2 C35E and IS 1570 (Part 4) 10Mo6?
Different category: EN 10083-2 C35E is Carbon Steel, IS 1570 (Part 4) 10Mo6 is Alloy Steel. EN 10083-2 C35E specifies Cr+Mo+Ni, P, S which are not specified for IS 1570 (Part 4) 10Mo6.
Can EN 10083-2 C35E be substituted with IS 1570 (Part 4) 10Mo6?
EN 10083-2 C35E and IS 1570 (Part 4) 10Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.