Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10083-2 C45 (EN 10083-2:2006) and BS 970 (Part 1) 060A32 (BS 970 (Part 1):1983) are both steel grades.
Both fall under the Carbon Steel category.
EN 10083-2 C45 is typically used for shafts, gears, bolts, machine parts, tools, while BS 970 (Part 1) 060A32 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6..
EN 10083-2 C45 is defined under European Standard (EN), originating from Europe, while BS 970 (Part 1) 060A32 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, EN 10083-2 C45 vs BS 970 (Part 1) 060A32 is a 64.7% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-2 C45
BS 970 (Part 1) 060A32
Condition
Quenched and tempered (+QT), ruling section d <= 16 mm
Not specified
Elongation
14% min
Not specified
Hardness
Soft annealed (+A): 207 HBW max
Not specified
Tensile Strength
700 to 850 MPa
Not specified
Yield Strength
490 MPa min
Not specified
Typical Applications
EN 10083-2 C45
Shafts, gears, bolts, machine parts, tools
BS 970 (Part 1) 060A32
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
EN 10083-2 C45 specifies Cr, Cr+Mo+Ni, Mo, Ni which are not specified for BS 970 (Part 1) 060A32.
Can EN 10083-2 C45 Be Substituted With BS 970 (Part 1) 060A32?
EN 10083-2 C45 and BS 970 (Part 1) 060A32 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-2 C45 and BS 970 (Part 1) 060A32?
EN 10083-2 C45 specifies Cr, Cr+Mo+Ni, Mo, Ni which are not specified for BS 970 (Part 1) 060A32.
Can EN 10083-2 C45 be substituted with BS 970 (Part 1) 060A32?
EN 10083-2 C45 and BS 970 (Part 1) 060A32 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.