EN 10083-3 30MnB5 vs BS 970 (Part 1) 173H16

Close Alternative — 80.1% match based on chemical composition and mechanical property overlap.

EN 10083-3 30MnB5 (EN 10083-3:2006) and BS 970 (Part 1) 173H16 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. EN 10083-3 30MnB5 is typically used for quenched and tempered, flame or induction hardened machine parts (clause 1), while BS 970 (Part 1) 173H16 is commonly used for case hardening steel supplied to specified hardenability limits (end quench test, table 10).. EN 10083-3 30MnB5 is defined under European Standard (EN), originating from Europe, while BS 970 (Part 1) 173H16 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, EN 10083-3 30MnB5 vs BS 970 (Part 1) 173H16 is a 80.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80.1%.

Frequently Compared With EN 10083-3 30MnB5:
IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
80.1%
MECHANICAL MATCH
No shared data
OVERALL
80.1%
Specifications
Property EN 10083-3 30MnB5 BS 970 (Part 1) 173H16
Standard EN 10083-3:2006 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
B (%) 0.0008-0.0050 0.0005-0.005
C (%) 0.27-0.33 0.13-0.19
Mn (%) 1.15-1.45 1.10-1.40
P (%) <=0.025 <=0.060
S (%) <=0.035 0.03-0.06
Si (%) <=0.40 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10083-3 30MnB5 BS 970 (Part 1) 173H16
Condition Quenched and tempered (+QT), ruling section d <= 16 mm Not specified
Elongation 13% min Not specified
Tensile Strength 950 to 1150 MPa Not specified
Yield Strength 800 MPa min Not specified
Typical Applications
EN 10083-3 30MnB5
Quenched and tempered, flame or induction hardened machine parts (clause 1)
BS 970 (Part 1) 173H16
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
Key Differences
Can EN 10083-3 30MnB5 Be Substituted With BS 970 (Part 1) 173H16?
EN 10083-3 30MnB5 and BS 970 (Part 1) 173H16 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10083-3 30MnB5
0 active listings and RFQs →
BS 970 (Part 1) 173H16
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10083-3 30MnB5 and BS 970 (Part 1) 173H16?
EN 10083-3 30MnB5 specifies Si which is not specified for BS 970 (Part 1) 173H16.
Can EN 10083-3 30MnB5 be substituted with BS 970 (Part 1) 173H16?
EN 10083-3 30MnB5 and BS 970 (Part 1) 173H16 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.