EN 10083-3 33MnCrB5-2 vs IS 4367 07Cr4Mo6

Minimal Match — 34.7% match based on chemical composition and mechanical property overlap.

EN 10083-3 33MnCrB5-2 (EN 10083-3:2006) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. EN 10083-3 33MnCrB5-2 is defined under European Standard (EN), originating from Europe, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10083-3 33MnCrB5-2 vs IS 4367 07Cr4Mo6 is a 52% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 34.7%.

Frequently Compared With EN 10083-3 33MnCrB5-2:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 11169 (Part 1) 10Ni5Cr4 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
52%
MECHANICAL MATCH
0%
OVERALL
34.7%
Specifications
Property EN 10083-3 33MnCrB5-2 IS 4367 07Cr4Mo6
Standard EN 10083-3:2006 IS 4367:1991
Category Alloy Steel Alloy Steel
B (%) 0.0008-0.0050 Not specified
C (%) 0.30-0.36 <=0.12
Cr (%) 0.30-0.60 0.70-1.10
Mn (%) 1.20-1.50 0.40-0.70
P (%) <=0.025 <=0.035
S (%) <=0.035 <=0.035
Si (%) <=0.40 0.15-0.60
Ni (%) Not specified <=0.30
Mo (%) Not specified 0.45-0.65
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10083-3 33MnCrB5-2 IS 4367 07Cr4Mo6
Condition Quenched and tempered (+QT), ruling section d <= 16 mm Normalised and tempered, ruling section up to 40 mm
Elongation 13% min >=19%
Tensile Strength 1050 to 1300 MPa 380-550 MPa
Yield Strength 850 MPa min 225 MPa min
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Typical Applications
EN 10083-3 33MnCrB5-2
Quenched and tempered, flame or induction hardened machine parts (clause 1)
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can EN 10083-3 33MnCrB5-2 Be Substituted With IS 4367 07Cr4Mo6?
EN 10083-3 33MnCrB5-2 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10083-3 33MnCrB5-2
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10083-3 33MnCrB5-2 and IS 4367 07Cr4Mo6?
EN 10083-3 33MnCrB5-2 specifies B which is not specified for IS 4367 07Cr4Mo6. IS 4367 07Cr4Mo6 specifies Ni, Mo which are not specified for EN 10083-3 33MnCrB5-2.
Can EN 10083-3 33MnCrB5-2 be substituted with IS 4367 07Cr4Mo6?
EN 10083-3 33MnCrB5-2 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.