Close Alternative — 81.9% match
based on chemical composition and mechanical property overlap.
EN 10083-3 34CrMoS4 (EN 10083-3:2006) and SAE J404 4135 (SAE J404:2009) are both steel grades.
Both fall under the Alloy Steel category.
EN 10083-3 34CrMoS4 is typically used for quenched and tempered, flame or induction hardened machine parts (clause 1), while SAE J404 4135 is commonly used for gears, shafts, pressure vessels, high tensile bolts.
EN 10083-3 34CrMoS4 is defined under European Standard (EN), originating from Europe, while SAE J404 4135 is defined under SAE International, originating from United States.
As per chemical composition, EN 10083-3 34CrMoS4 vs SAE J404 4135 is a 81.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 81.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-3 34CrMoS4
SAE J404 4135
Condition
Quenched and tempered (+QT), ruling section d <= 16 mm
Not specified
Elongation
11% min
Not specified
Hardness
Soft annealed (+A): 223 HBW max
Not specified
Tensile Strength
1000 to 1200 MPa
Not specified
Yield Strength
800 MPa min
Not specified
Typical Applications
EN 10083-3 34CrMoS4
Quenched and tempered, flame or induction hardened machine parts (clause 1)
SAE J404 4135
Gears, shafts, pressure vessels, high tensile bolts
Can EN 10083-3 34CrMoS4 Be Substituted With SAE J404 4135?
EN 10083-3 34CrMoS4 and SAE J404 4135 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10083-3 34CrMoS4 and SAE J404 4135?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10083-3 34CrMoS4 be substituted with SAE J404 4135?
EN 10083-3 34CrMoS4 and SAE J404 4135 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.