Minimal Match — 49% match
based on chemical composition and mechanical property overlap.
EN 10083-3 46Cr2 (EN 10083-3:2006) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades.
Both fall under the Alloy Steel category.
EN 10083-3 46Cr2 is typically used for quenched and tempered, flame or induction hardened machine parts (clause 1), while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components.
EN 10083-3 46Cr2 is defined under European Standard (EN), originating from Europe, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.
As per chemical composition, EN 10083-3 46Cr2 vs UNI 11234 100Cr6 is a 73.5% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 49%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-3 46Cr2
UNI 11234 100Cr6
Condition
Quenched and tempered (+QT), ruling section d <= 16 mm
Not specified
Elongation
12% min
10-14 %
Hardness
Soft annealed (+A): 223 HBW max
60-64 HRC
Tensile Strength
900 to 1100 MPa
750-1000 MPa
Yield Strength
650 MPa min
400-600 MPa
Typical Applications
EN 10083-3 46Cr2
Quenched and tempered, flame or induction hardened machine parts (clause 1)
Can EN 10083-3 46Cr2 Be Substituted With UNI 11234 100Cr6?
EN 10083-3 46Cr2 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-3 46Cr2 and UNI 11234 100Cr6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10083-3 46Cr2 be substituted with UNI 11234 100Cr6?
EN 10083-3 46Cr2 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.