Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10083-3 42CrMo4 (EN 10083-3:2006) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades.
Both fall under the Alloy Steel category.
EN 10083-3 42CrMo4 is typically used for high strength bolts, crankshafts, axles, while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components.
EN 10083-3 42CrMo4 is defined under European Standard (EN), originating from Europe, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.
As per chemical composition, EN 10083-3 42CrMo4 vs UNI 11234 100Cr6 is a 64.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-3 42CrMo4
UNI 11234 100Cr6
Condition
Quenched and tempered (+QT), ruling section d <= 16 mm
EN 10083-3 42CrMo4 specifies Mo which is not specified for UNI 11234 100Cr6.
Can EN 10083-3 42CrMo4 Be Substituted With UNI 11234 100Cr6?
EN 10083-3 42CrMo4 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10083-3 42CrMo4 and UNI 11234 100Cr6?
EN 10083-3 42CrMo4 specifies Mo which is not specified for UNI 11234 100Cr6.
Can EN 10083-3 42CrMo4 be substituted with UNI 11234 100Cr6?
EN 10083-3 42CrMo4 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.