EN 10084 20NiCrMo13-4 vs IS 4367 10Cr9Mo10

Minimal Match — 40.6% match based on chemical composition and mechanical property overlap.

EN 10084 20NiCrMo13-4 (EN 10084:2008) and IS 4367 10Cr9Mo10 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. EN 10084 20NiCrMo13-4 is defined under European Standard (EN), originating from Europe, while IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10084 20NiCrMo13-4 vs IS 4367 10Cr9Mo10 is a 60.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 40.6%.

Frequently Compared With EN 10084 20NiCrMo13-4:
NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
60.9%
MECHANICAL MATCH
0%
OVERALL
40.6%
Specifications
Property EN 10084 20NiCrMo13-4 IS 4367 10Cr9Mo10
Standard EN 10084:2008 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.17-0.22 <=0.15
Cr (%) 0.80-1.20 2.00-2.50
Mn (%) 0.30-0.60 0.40-0.70
Mo (%) 0.30-0.50 0.90-1.10
Ni (%) 3.00-3.50 <=0.30
P (%) <=0.025 <=0.035
S (%) <=0.035 <=0.035
Si (%) <=0.40 <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10084 20NiCrMo13-4 IS 4367 10Cr9Mo10
Condition Soft annealed Normalised and tempered, ruling section up to 50 mm
Hardenability +H band at 1.5 mm from the quenched end: 43 to 53 HRC Not specified
Hardness Soft annealed: 255 HB max Not specified
Tensile Strength Not specified 410-590 MPa
Yield Strength Not specified 245 MPa min
Elongation Not specified >=18%
Izod Impact Not specified 55 J min
Hardness (soft annealed) Not specified <=187 HB
Typical Applications
EN 10084 20NiCrMo13-4
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
IS 4367 10Cr9Mo10
Not documented
Can EN 10084 20NiCrMo13-4 Be Substituted With IS 4367 10Cr9Mo10?
EN 10084 20NiCrMo13-4 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10084 20NiCrMo13-4
0 active listings and RFQs →
IS 4367 10Cr9Mo10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10084 20NiCrMo13-4 and IS 4367 10Cr9Mo10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10084 20NiCrMo13-4 be substituted with IS 4367 10Cr9Mo10?
EN 10084 20NiCrMo13-4 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.