EN 10084 22CrMoS3-5 vs IS 4367 07Cr4Mo6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10084 22CrMoS3-5 (EN 10084:2008) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. EN 10084 22CrMoS3-5 is defined under European Standard (EN), originating from Europe, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10084 22CrMoS3-5 vs IS 4367 07Cr4Mo6 is a 63.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10084 22CrMoS3-5:
IS 1570 (Part 7) 12Cr4Mo5H NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
63.6%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10084 22CrMoS3-5 IS 4367 07Cr4Mo6
Standard EN 10084:2008 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.19-0.24 <=0.12
Cr (%) 0.70-1.00 0.70-1.10
Mn (%) 0.70-1.00 0.40-0.70
Mo (%) 0.40-0.50 0.45-0.65
P (%) <=0.025 <=0.035
S (%) 0.020-0.040 <=0.035
Si (%) <=0.40 0.15-0.60
Ni (%) Not specified <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10084 22CrMoS3-5 IS 4367 07Cr4Mo6
Condition Soft annealed Normalised and tempered, ruling section up to 40 mm
Hardenability +H band at 1.5 mm from the quenched end: 42 to 50 HRC Not specified
Hardness Soft annealed: 217 HB max Not specified
Tensile Strength Not specified 380-550 MPa
Yield Strength Not specified 225 MPa min
Elongation Not specified >=19%
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Typical Applications
EN 10084 22CrMoS3-5
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can EN 10084 22CrMoS3-5 Be Substituted With IS 4367 07Cr4Mo6?
EN 10084 22CrMoS3-5 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10084 22CrMoS3-5
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10084 22CrMoS3-5 and IS 4367 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies Ni which is not specified for EN 10084 22CrMoS3-5.
Can EN 10084 22CrMoS3-5 be substituted with IS 4367 07Cr4Mo6?
EN 10084 22CrMoS3-5 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.