EN 10088-1 X10CrAlSi13 vs EN 10088-1 1.4006

Close Alternative — 74.4% match based on chemical composition and mechanical property overlap.

EN 10088-1 X10CrAlSi13 (EN 10088-1:2014) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X10CrAlSi13 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X10CrAlSi13 vs EN 10088-1 1.4006 is a 74.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 74.4%.

Frequently Compared With EN 10088-1 X10CrAlSi13:
EN 10088-1 1.4845 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
74.4%
MECHANICAL MATCH
No shared data
OVERALL
74.4%
Specifications
Property EN 10088-1 X10CrAlSi13 EN 10088-1 1.4006
Standard EN 10088-1:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.12 0.08–0.15
Si (%) 0.70-1.40 ≤1.00
Mn (%) <=1.00 ≤1.50
P (%) <=0.040 Not specified
S (%) <=0.015 Not specified
Cr (%) 12.0-14.0 11.5–13.5
Al (%) 0.70-1.20 Not specified
Ni (%) Not specified ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X10CrAlSi13 EN 10088-1 1.4006
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Elongation Not specified ≥18%
Typical Applications
EN 10088-1 X10CrAlSi13
Not documented
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can EN 10088-1 X10CrAlSi13 Be Substituted With EN 10088-1 1.4006?
EN 10088-1 X10CrAlSi13 and EN 10088-1 1.4006 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
EN 10088-1 X10CrAlSi13
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
EN 10088-1 X10CrAlSi13
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X10CrAlSi13 and EN 10088-1 1.4006?
EN 10088-1 X10CrAlSi13 specifies P, S, Al which are not specified for EN 10088-1 1.4006. EN 10088-1 1.4006 specifies Ni which is not specified for EN 10088-1 X10CrAlSi13.
Can EN 10088-1 X10CrAlSi13 be substituted with EN 10088-1 1.4006?
EN 10088-1 X10CrAlSi13 and EN 10088-1 1.4006 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.