EN 10088-1 X11CrNiMnN19-8-6 vs IS 6603 X11Cr19Ni8Mn6N

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-1 X11CrNiMnN19-8-6 (EN 10088-1:2014) and IS 6603 X11Cr19Ni8Mn6N (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X11CrNiMnN19-8-6 is defined under European Standard (EN), originating from Europe, while IS 6603 X11Cr19Ni8Mn6N is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X11CrNiMnN19-8-6 vs IS 6603 X11Cr19Ni8Mn6N is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-1 X11CrNiMnN19-8-6:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-1 X11CrNiMnN19-8-6 IS 6603 X11Cr19Ni8Mn6N
Standard EN 10088-1:2014 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 0.07-0.15
Si (%) 0.50-1.00 0.50-1.00
Mn (%) 5.0-7.5 5.0-7.5
P (%) <=0.030 <=0.030
S (%) <=0.015 <=0.015
Cr (%) 17.5-19.5 17.5-19.5
Ni (%) 6.5-8.5 6.5-8.5
N (%) 0.20-0.30 0.20-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X11CrNiMnN19-8-6 IS 6603 X11Cr19Ni8Mn6N
Tensile Strength Not specified 750-950 MPa
Yield Strength Not specified >=340 MPa
Condition Not specified Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 15 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-1 X11CrNiMnN19-8-6
Not documented
IS 6603 X11Cr19Ni8Mn6N
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-1 X11CrNiMnN19-8-6 Be Substituted With IS 6603 X11Cr19Ni8Mn6N?
EN 10088-1 X11CrNiMnN19-8-6 and IS 6603 X11Cr19Ni8Mn6N overlap closely enough on chemistry and mechanical properties that IS 6603 X11Cr19Ni8Mn6N is often considered as a substitute for EN 10088-1 X11CrNiMnN19-8-6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X11CrNiMnN19-8-6
0 active listings and RFQs →
IS 6603 X11Cr19Ni8Mn6N
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X11CrNiMnN19-8-6 and IS 6603 X11Cr19Ni8Mn6N?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X11CrNiMnN19-8-6 be substituted with IS 6603 X11Cr19Ni8Mn6N?
EN 10088-1 X11CrNiMnN19-8-6 and IS 6603 X11Cr19Ni8Mn6N overlap closely enough on chemistry and mechanical properties that IS 6603 X11Cr19Ni8Mn6N is often considered as a substitute for EN 10088-1 X11CrNiMnN19-8-6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.