Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X1CrNi25-21 (EN 10088-1:2014) and IS 6603 X01Cr25Ni22Mo2 (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X1CrNi25-21 is defined under European Standard (EN), originating from Europe, while IS 6603 X01Cr25Ni22Mo2 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X1CrNi25-21 vs IS 6603 X01Cr25Ni22Mo2 is a 77% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X1CrNi25-21
IS 6603 X01Cr25Ni22Mo2
Tensile Strength
Not specified
540-740 MPa
Yield Strength
Not specified
>=250 MPa
Elongation
Not specified
>=35%
Condition
Not specified
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-1 X1CrNi25-21
Not documented
IS 6603 X01Cr25Ni22Mo2
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-1 X1CrNi25-21 Be Substituted With IS 6603 X01Cr25Ni22Mo2?
EN 10088-1 X1CrNi25-21 and IS 6603 X01Cr25Ni22Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 X1CrNi25-21 and IS 6603 X01Cr25Ni22Mo2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X1CrNi25-21 be substituted with IS 6603 X01Cr25Ni22Mo2?
EN 10088-1 X1CrNi25-21 and IS 6603 X01Cr25Ni22Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.