EN 10088-1 X1CrNiMoN25-22-2 vs EN 10088-3 X1CrNiMoN25-22-2

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-1 X1CrNiMoN25-22-2 (EN 10088-1:2014) and EN 10088-3 X1CrNiMoN25-22-2 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X1CrNiMoN25-22-2 is defined under European Standard (EN), originating from Europe, while EN 10088-3 X1CrNiMoN25-22-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X1CrNiMoN25-22-2 vs EN 10088-3 X1CrNiMoN25-22-2 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-1 X1CrNiMoN25-22-2:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-1 X1CrNiMoN25-22-2 EN 10088-3 X1CrNiMoN25-22-2
Standard EN 10088-1:2014 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.70 <=0.70
Mn (%) <=2.00 <=2.00
P (%) <=0.025 <=0.025
S (%) <=0.010 <=0.010
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 2.00-2.50 2.00-2.50
Ni (%) 21.0-23.0 21.0-23.0
N (%) 0.10-0.16 0.10-0.16
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X1CrNiMoN25-22-2 EN 10088-3 X1CrNiMoN25-22-2
Tensile Strength Not specified 540-740 MPa
Yield Strength Not specified >=250 MPa
Elongation Not specified >=35%
Hardness Not specified <=240 HB
Condition Not specified Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
EN 10088-1 X1CrNiMoN25-22-2
Not documented
EN 10088-3 X1CrNiMoN25-22-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can EN 10088-1 X1CrNiMoN25-22-2 Be Substituted With EN 10088-3 X1CrNiMoN25-22-2?
EN 10088-1 X1CrNiMoN25-22-2 and EN 10088-3 X1CrNiMoN25-22-2 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X1CrNiMoN25-22-2 is often considered as a substitute for EN 10088-1 X1CrNiMoN25-22-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X1CrNiMoN25-22-2
0 active listings and RFQs →
EN 10088-3 X1CrNiMoN25-22-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X1CrNiMoN25-22-2 and EN 10088-3 X1CrNiMoN25-22-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X1CrNiMoN25-22-2 be substituted with EN 10088-3 X1CrNiMoN25-22-2?
EN 10088-1 X1CrNiMoN25-22-2 and EN 10088-3 X1CrNiMoN25-22-2 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X1CrNiMoN25-22-2 is often considered as a substitute for EN 10088-1 X1CrNiMoN25-22-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.