EN 10088-1 X2CrMnNiMoN21-5-3 vs EN 10088-2 X2CrMnNiMoN21-5-3

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrMnNiMoN21-5-3 (EN 10088-1:2014) and EN 10088-2 X2CrMnNiMoN21-5-3 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrMnNiMoN21-5-3 is defined under European Standard (EN), originating from Europe, while EN 10088-2 X2CrMnNiMoN21-5-3 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X2CrMnNiMoN21-5-3 vs EN 10088-2 X2CrMnNiMoN21-5-3 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-1 X2CrMnNiMoN21-5-3:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-1 X2CrMnNiMoN21-5-3 EN 10088-2 X2CrMnNiMoN21-5-3
Standard EN 10088-1:2014 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 4.0-6.0 4.0-6.0
P (%) <=0.035 <=0.035
S (%) <=0.030 <=0.030
Cr (%) 19.5-21.5 19.5-21.5
Mo (%) 0.10-0.60 0.10-0.60
Ni (%) 1.50-3.50 1.50-3.50
N (%) 0.05-0.20 0.05-0.20
Cu (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrMnNiMoN21-5-3 EN 10088-2 X2CrMnNiMoN21-5-3
Tensile Strength Not specified 700-900 MPa
Yield Strength Not specified >=500 MPa
Elongation Not specified >=20%
Condition Not specified Solution annealed (+AT), cold rolled strip, up to 6.4 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Typical Applications
EN 10088-1 X2CrMnNiMoN21-5-3
Not documented
EN 10088-2 X2CrMnNiMoN21-5-3
General purposes, hot or cold rolled sheet/plate and strip
Can EN 10088-1 X2CrMnNiMoN21-5-3 Be Substituted With EN 10088-2 X2CrMnNiMoN21-5-3?
EN 10088-1 X2CrMnNiMoN21-5-3 and EN 10088-2 X2CrMnNiMoN21-5-3 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrMnNiMoN21-5-3 is often considered as a substitute for EN 10088-1 X2CrMnNiMoN21-5-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrMnNiMoN21-5-3
0 active listings and RFQs →
EN 10088-2 X2CrMnNiMoN21-5-3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrMnNiMoN21-5-3 and EN 10088-2 X2CrMnNiMoN21-5-3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X2CrMnNiMoN21-5-3 be substituted with EN 10088-2 X2CrMnNiMoN21-5-3?
EN 10088-1 X2CrMnNiMoN21-5-3 and EN 10088-2 X2CrMnNiMoN21-5-3 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X2CrMnNiMoN21-5-3 is often considered as a substitute for EN 10088-1 X2CrMnNiMoN21-5-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.