EN 10088-1 X2CrMnNiN17-7-5 vs ASTM A240/A240M S20153

Strong Match — 90.1% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrMnNiN17-7-5 (EN 10088-1:2014) and ASTM A240/A240M S20153 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrMnNiN17-7-5 is defined under European Standard (EN), originating from Europe, while ASTM A240/A240M S20153 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X2CrMnNiN17-7-5 vs ASTM A240/A240M S20153 is a 90.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.1%.

Frequently Compared With EN 10088-1 X2CrMnNiN17-7-5:
ASTM A959 201LN ASTM A959 201L ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301
Match Breakdown
CHEMISTRY MATCH
90.1%
MECHANICAL MATCH
No shared data
OVERALL
90.1%
Specifications
Property EN 10088-1 X2CrMnNiN17-7-5 ASTM A240/A240M S20153
Standard EN 10088-1:2014 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.03
Si (%) <=1.00 <=0.75
Mn (%) 6.0-8.0 6.40-7.50
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 16.0-17.5 16.0-17.5
Ni (%) 3.5-5.5 4.0-5.0
N (%) 0.15-0.25 0.10-0.25
Cu (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrMnNiN17-7-5 ASTM A240/A240M S20153
Tensile Strength Not specified >=655 MPa
Yield Strength Not specified >=310 MPa
Elongation Not specified >=45%
Hardness Not specified <=241 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
EN 10088-1 X2CrMnNiN17-7-5
Not documented
ASTM A240/A240M S20153
Pressure vessels and general applications (plate, sheet and strip)
Can EN 10088-1 X2CrMnNiN17-7-5 Be Substituted With ASTM A240/A240M S20153?
EN 10088-1 X2CrMnNiN17-7-5 and ASTM A240/A240M S20153 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S20153 is often considered as a substitute for EN 10088-1 X2CrMnNiN17-7-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrMnNiN17-7-5
0 active listings and RFQs →
ASTM A240/A240M S20153
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrMnNiN17-7-5 and ASTM A240/A240M S20153?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X2CrMnNiN17-7-5 be substituted with ASTM A240/A240M S20153?
EN 10088-1 X2CrMnNiN17-7-5 and ASTM A240/A240M S20153 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S20153 is often considered as a substitute for EN 10088-1 X2CrMnNiN17-7-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.