Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X2CrMnNiN21-5-1 (EN 10088-1:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X2CrMnNiN21-5-1 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-1 X2CrMnNiN21-5-1 vs GOST 5632 06Kh23N28 is a 51.7% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With EN 10088-1 X2CrMnNiN21-5-1:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X2CrMnNiN21-5-1
GOST 5632 06Kh23N28
Tensile Strength
Not specified
≥510 MPa
Yield Strength
Not specified
≥196 MPa
Elongation
Not specified
≥35%
Max Service Temp
Not specified
1050°C
Typical Applications
EN 10088-1 X2CrMnNiN21-5-1
Not documented
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
EN 10088-1 X2CrMnNiN21-5-1 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-1 X2CrMnNiN21-5-1 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-1 X2CrMnNiN21-5-1 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 X2CrMnNiN21-5-1 and GOST 5632 06Kh23N28?
EN 10088-1 X2CrMnNiN21-5-1 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-1 X2CrMnNiN21-5-1 be substituted with GOST 5632 06Kh23N28?
EN 10088-1 X2CrMnNiN21-5-1 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.