EN 10088-1 X2CrMoTi18-2 vs IS 6603 X02Cr18Mo2TiS

Close Alternative — 78.7% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrMoTi18-2 (EN 10088-1:2014) and IS 6603 X02Cr18Mo2TiS (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrMoTi18-2 is defined under European Standard (EN), originating from Europe, while IS 6603 X02Cr18Mo2TiS is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X2CrMoTi18-2 vs IS 6603 X02Cr18Mo2TiS is a 78.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 78.7%.

Frequently Compared With EN 10088-1 X2CrMoTi18-2:
ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
78.7%
MECHANICAL MATCH
No shared data
OVERALL
78.7%
Specifications
Property EN 10088-1 X2CrMoTi18-2 IS 6603 X02Cr18Mo2TiS
Standard EN 10088-1:2014 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) <=0.025 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=0.50
P (%) <=0.040 <=0.040
S (%) <=0.015 >=0.15
Cr (%) 17.0-20.0 17.5-19.0
Mo (%) 1.80-2.50 2.00-2.50
N (%) <=0.030 Not specified
Ti (%) Not specified 0.30-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrMoTi18-2 IS 6603 X02Cr18Mo2TiS
Tensile Strength Not specified >=430 MPa
Yield Strength Not specified >=280 MPa
Elongation Not specified >=15%
Hardness Not specified <=200 HB
Condition Not specified Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Tensile Strength is a minimum as printed
Typical Applications
EN 10088-1 X2CrMoTi18-2
Not documented
IS 6603 X02Cr18Mo2TiS
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
Can EN 10088-1 X2CrMoTi18-2 Be Substituted With IS 6603 X02Cr18Mo2TiS?
EN 10088-1 X2CrMoTi18-2 and IS 6603 X02Cr18Mo2TiS are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-1 X2CrMoTi18-2
0 active listings and RFQs →
IS 6603 X02Cr18Mo2TiS
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrMoTi18-2 and IS 6603 X02Cr18Mo2TiS?
EN 10088-1 X2CrMoTi18-2 specifies N which is not specified for IS 6603 X02Cr18Mo2TiS. IS 6603 X02Cr18Mo2TiS specifies Ti which is not specified for EN 10088-1 X2CrMoTi18-2.
Can EN 10088-1 X2CrMoTi18-2 be substituted with IS 6603 X02Cr18Mo2TiS?
EN 10088-1 X2CrMoTi18-2 and IS 6603 X02Cr18Mo2TiS are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.