EN 10088-1 X2CrNi19-11 vs ASTM A276/A276M S30403

Strong Match — 91.7% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrNi19-11 (EN 10088-1:2014) and ASTM A276/A276M S30403 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrNi19-11 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S30403 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X2CrNi19-11 vs ASTM A276/A276M S30403 is a 91.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91.7%.

Frequently Compared With EN 10088-1 X2CrNi19-11:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
91.7%
MECHANICAL MATCH
No shared data
OVERALL
91.7%
Specifications
Property EN 10088-1 X2CrNi19-11 ASTM A276/A276M S30403
Standard EN 10088-1:2014 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 18.0-20.0 18.0-20.0
Ni (%) 10.0-12.0 8.0-12.0
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrNi19-11 ASTM A276/A276M S30403
Tensile Strength Not specified >=485 MPa
Yield Strength Not specified >=170 MPa
Elongation Not specified >=40%
Condition Not specified Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
EN 10088-1 X2CrNi19-11
Not documented
ASTM A276/A276M S30403
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can EN 10088-1 X2CrNi19-11 Be Substituted With ASTM A276/A276M S30403?
EN 10088-1 X2CrNi19-11 and ASTM A276/A276M S30403 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S30403 is often considered as a substitute for EN 10088-1 X2CrNi19-11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrNi19-11
0 active listings and RFQs →
ASTM A276/A276M S30403
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrNi19-11 and ASTM A276/A276M S30403?
EN 10088-1 X2CrNi19-11 specifies N which is not specified for ASTM A276/A276M S30403.
Can EN 10088-1 X2CrNi19-11 be substituted with ASTM A276/A276M S30403?
EN 10088-1 X2CrNi19-11 and ASTM A276/A276M S30403 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S30403 is often considered as a substitute for EN 10088-1 X2CrNi19-11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.