EN 10088-1 X2CrNiMnMoN25-18-6-5 vs ASTM A276/A276M S34565

Strong Match — 87% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrNiMnMoN25-18-6-5 (EN 10088-1:2014) and ASTM A276/A276M S34565 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S34565 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X2CrNiMnMoN25-18-6-5 vs ASTM A276/A276M S34565 is a 87% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87%.

Frequently Compared With EN 10088-1 X2CrNiMnMoN25-18-6-5:
EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
87%
MECHANICAL MATCH
No shared data
OVERALL
87%
Specifications
Property EN 10088-1 X2CrNiMnMoN25-18-6-5 ASTM A276/A276M S34565
Standard EN 10088-1:2014 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 5.0-7.0 5.0-7.0
P (%) <=0.030 <=0.030
S (%) <=0.015 <=0.010
Cr (%) 24.0-26.0 23.0-25.0
Mo (%) 4.0-5.0 4.0-5.0
Ni (%) 16.0-19.0 16.0-18.0
N (%) 0.30-0.60 0.40-0.60
Nb (%) <=0.15 <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrNiMnMoN25-18-6-5 ASTM A276/A276M S34565
Tensile Strength Not specified >=795 MPa
Yield Strength Not specified >=415 MPa
Elongation Not specified >=35%
Typical Applications
EN 10088-1 X2CrNiMnMoN25-18-6-5
Not documented
ASTM A276/A276M S34565
Stainless steel bars and shapes (hot-finished or cold-finished)
Can EN 10088-1 X2CrNiMnMoN25-18-6-5 Be Substituted With ASTM A276/A276M S34565?
EN 10088-1 X2CrNiMnMoN25-18-6-5 and ASTM A276/A276M S34565 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S34565 is often considered as a substitute for EN 10088-1 X2CrNiMnMoN25-18-6-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
ASTM A276/A276M S34565
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrNiMnMoN25-18-6-5 and ASTM A276/A276M S34565?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X2CrNiMnMoN25-18-6-5 be substituted with ASTM A276/A276M S34565?
EN 10088-1 X2CrNiMnMoN25-18-6-5 and ASTM A276/A276M S34565 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S34565 is often considered as a substitute for EN 10088-1 X2CrNiMnMoN25-18-6-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.