EN 10088-1 X2CrNiMoN25-7-4 vs JIS G4304 SUS327L1

Strong Match — 89.9% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrNiMoN25-7-4 (EN 10088-1:2014) and JIS G4304 SUS327L1 (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrNiMoN25-7-4 is defined under European Standard (EN), originating from Europe, while JIS G4304 SUS327L1 is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, EN 10088-1 X2CrNiMoN25-7-4 vs JIS G4304 SUS327L1 is a 89.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.9%.

Frequently Compared With EN 10088-1 X2CrNiMoN25-7-4:
ASTM A959 2507 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- EN 10088-1 1.4301 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
89.9%
MECHANICAL MATCH
No shared data
OVERALL
89.9%
Specifications
Property EN 10088-1 X2CrNiMoN25-7-4 JIS G4304 SUS327L1
Standard EN 10088-1:2014 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=0.80
Mn (%) <=2.00 <=1.20
P (%) <=0.035 <=0.035
S (%) <=0.015 <=0.020
Cr (%) 24.0-26.0 24.00-26.00
Mo (%) 3.0-4.5 3.00-5.00
Ni (%) 6.0-8.0 6.00-8.00
N (%) 0.24-0.35 0.24-0.32
Cu (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrNiMoN25-7-4 JIS G4304 SUS327L1
Tensile Strength Not specified >=795 MPa
Yield Strength Not specified >=550 MPa
Elongation Not specified >=15%
Hardness Not specified <=310 HB
Condition Not specified Solution heat treated plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
EN 10088-1 X2CrNiMoN25-7-4
Not documented
JIS G4304 SUS327L1
Hot-rolled stainless steel plates and strips
Key Differences
Can EN 10088-1 X2CrNiMoN25-7-4 Be Substituted With JIS G4304 SUS327L1?
EN 10088-1 X2CrNiMoN25-7-4 and JIS G4304 SUS327L1 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS327L1 is often considered as a substitute for EN 10088-1 X2CrNiMoN25-7-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrNiMoN25-7-4
0 active listings and RFQs →
JIS G4304 SUS327L1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrNiMoN25-7-4 and JIS G4304 SUS327L1?
JIS G4304 SUS327L1 specifies Cu which is not specified for EN 10088-1 X2CrNiMoN25-7-4.
Can EN 10088-1 X2CrNiMoN25-7-4 be substituted with JIS G4304 SUS327L1?
EN 10088-1 X2CrNiMoN25-7-4 and JIS G4304 SUS327L1 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS327L1 is often considered as a substitute for EN 10088-1 X2CrNiMoN25-7-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.