Strong Match — 95.3% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X2CrNiN18-10 (EN 10088-1:2014) and JIS G4305 SUS304LN (JIS G4305:2012) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X2CrNiN18-10 is defined under European Standard (EN), originating from Europe, while JIS G4305 SUS304LN is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, EN 10088-1 X2CrNiN18-10 vs JIS G4305 SUS304LN is a 95.3% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 95.3%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X2CrNiN18-10
JIS G4305 SUS304LN
Tensile Strength
Not specified
>=550 MPa
Yield Strength
Not specified
>=245 MPa
Elongation
Not specified
>=40%
Hardness
Not specified
<=217 HB
Condition
Not specified
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
EN 10088-1 X2CrNiN18-10
Not documented
JIS G4305 SUS304LN
Cold-rolled stainless steel plates, sheet and strip
Can EN 10088-1 X2CrNiN18-10 Be Substituted With JIS G4305 SUS304LN?
EN 10088-1 X2CrNiN18-10 and JIS G4305 SUS304LN overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS304LN is often considered as a substitute for EN 10088-1 X2CrNiN18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X2CrNiN18-10 and JIS G4305 SUS304LN?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X2CrNiN18-10 be substituted with JIS G4305 SUS304LN?
EN 10088-1 X2CrNiN18-10 and JIS G4305 SUS304LN overlap closely enough on chemistry and mechanical properties that JIS G4305 SUS304LN is often considered as a substitute for EN 10088-1 X2CrNiN18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.