EN 10088-1 X2CrTi17 vs EN 10088-3 X2CrTi17

Strong Match — 94.8% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrTi17 (EN 10088-1:2014) and EN 10088-3 X2CrTi17 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrTi17 is defined under European Standard (EN), originating from Europe, while EN 10088-3 X2CrTi17 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X2CrTi17 vs EN 10088-3 X2CrTi17 is a 94.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.8%.

Frequently Compared With EN 10088-1 X2CrTi17:
GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
94.8%
MECHANICAL MATCH
No shared data
OVERALL
94.8%
Specifications
Property EN 10088-1 X2CrTi17 EN 10088-3 X2CrTi17
Standard EN 10088-1:2014 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.025 <=0.025
Si (%) <=0.50 <=0.50
Mn (%) <=0.50 <=0.50
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.015
Cr (%) 16.0-18.0 16.0-18.0
N (%) <=0.015 <=0.015
Ti (%) Not specified <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrTi17 EN 10088-3 X2CrTi17
Tensile Strength Not specified 420-620 MPa
Yield Strength Not specified >=200 MPa
Elongation Not specified >=20%
Hardness Not specified <=200 HB
Condition Not specified Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 50 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
EN 10088-1 X2CrTi17
Not documented
EN 10088-3 X2CrTi17
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Key Differences
Can EN 10088-1 X2CrTi17 Be Substituted With EN 10088-3 X2CrTi17?
EN 10088-1 X2CrTi17 and EN 10088-3 X2CrTi17 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X2CrTi17 is often considered as a substitute for EN 10088-1 X2CrTi17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrTi17
0 active listings and RFQs →
EN 10088-3 X2CrTi17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrTi17 and EN 10088-3 X2CrTi17?
EN 10088-3 X2CrTi17 specifies Ti which is not specified for EN 10088-1 X2CrTi17.
Can EN 10088-1 X2CrTi17 be substituted with EN 10088-3 X2CrTi17?
EN 10088-1 X2CrTi17 and EN 10088-3 X2CrTi17 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X2CrTi17 is often considered as a substitute for EN 10088-1 X2CrTi17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.