EN 10088-1 X3CrNiMo13-4 vs ASTM A276/A276M S41500

Close Alternative — 76.1% match based on chemical composition and mechanical property overlap.

EN 10088-1 X3CrNiMo13-4 (EN 10088-1:2014) and ASTM A276/A276M S41500 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X3CrNiMo13-4 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S41500 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X3CrNiMo13-4 vs ASTM A276/A276M S41500 is a 76.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.1%.

Frequently Compared With EN 10088-1 X3CrNiMo13-4:
ASTM A959 25-4-4 GB/T 3280 06Cr19Ni10 ASTM A959 .- EN 10088-1 1.4401 EN 10088-1 1.4845 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
76.1%
MECHANICAL MATCH
No shared data
OVERALL
76.1%
Specifications
Property EN 10088-1 X3CrNiMo13-4 ASTM A276/A276M S41500
Standard EN 10088-1:2014 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Si (%) <=0.70 <=0.60
Mn (%) <=1.50 0.50-1.00
P (%) <=0.040 <=0.030
S (%) <=0.015 <=0.030
Cr (%) 12.0-14.0 11.5-14.0
Mo (%) 0.30-0.70 0.50-1.00
Ni (%) 3.5-4.5 3.5-5.5
N (%) >=0.020 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X3CrNiMo13-4 ASTM A276/A276M S41500
Tensile Strength Not specified >=795 MPa
Yield Strength Not specified >=620 MPa
Elongation Not specified >=15%
Hardness Not specified <=295 HB
Condition Not specified Condition T (Hardened and tempered, higher temperature), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
EN 10088-1 X3CrNiMo13-4
Not documented
ASTM A276/A276M S41500
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can EN 10088-1 X3CrNiMo13-4 Be Substituted With ASTM A276/A276M S41500?
EN 10088-1 X3CrNiMo13-4 and ASTM A276/A276M S41500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-1 X3CrNiMo13-4
0 active listings and RFQs →
ASTM A276/A276M S41500
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X3CrNiMo13-4 and ASTM A276/A276M S41500?
EN 10088-1 X3CrNiMo13-4 specifies N which is not specified for ASTM A276/A276M S41500.
Can EN 10088-1 X3CrNiMo13-4 be substituted with ASTM A276/A276M S41500?
EN 10088-1 X3CrNiMo13-4 and ASTM A276/A276M S41500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.