Strong Match — 92.8% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X5CrNi17-7 (EN 10088-1:2014) and IS 6911 X10Cr17Ni7 (IS 6911:1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X5CrNi17-7 is defined under European Standard (EN), originating from Europe, while IS 6911 X10Cr17Ni7 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X5CrNi17-7 vs IS 6911 X10Cr17Ni7 is a 92.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 92.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X5CrNi17-7
IS 6911 X10Cr17Ni7
Bend Test (180 deg)
Not specified
Not required
Elongation (50 mm, annealed)
Not specified
>=40%
Hardness (annealed, max)
Not specified
212 HBS
Tensile Strength (annealed)
Not specified
>=590 MPa
Yield Strength (0.2% proof, annealed)
Not specified
>=220 MPa
Typical Applications
EN 10088-1 X5CrNi17-7
Not documented
IS 6911 X10Cr17Ni7
Stainless and heat-resisting steel plate, sheet and strip (clause 1.1)
Key Differences
EN 10088-1 X5CrNi17-7 specifies N which is not specified for IS 6911 X10Cr17Ni7.
Can EN 10088-1 X5CrNi17-7 Be Substituted With IS 6911 X10Cr17Ni7?
EN 10088-1 X5CrNi17-7 and IS 6911 X10Cr17Ni7 overlap closely enough on chemistry and mechanical properties that IS 6911 X10Cr17Ni7 is often considered as a substitute for EN 10088-1 X5CrNi17-7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X5CrNi17-7 and IS 6911 X10Cr17Ni7?
EN 10088-1 X5CrNi17-7 specifies N which is not specified for IS 6911 X10Cr17Ni7.
Can EN 10088-1 X5CrNi17-7 be substituted with IS 6911 X10Cr17Ni7?
EN 10088-1 X5CrNi17-7 and IS 6911 X10Cr17Ni7 overlap closely enough on chemistry and mechanical properties that IS 6911 X10Cr17Ni7 is often considered as a substitute for EN 10088-1 X5CrNi17-7 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.