EN 10088-1 X5CrNiMoTi15-2 vs ASTM A276/A276M S42010

Related Material — 69.7% match based on chemical composition and mechanical property overlap.

EN 10088-1 X5CrNiMoTi15-2 (EN 10088-1:2014) and ASTM A276/A276M S42010 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X5CrNiMoTi15-2 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S42010 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X5CrNiMoTi15-2 vs ASTM A276/A276M S42010 is a 69.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.7%.

Frequently Compared With EN 10088-1 X5CrNiMoTi15-2:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
69.7%
MECHANICAL MATCH
No shared data
OVERALL
69.7%
Specifications
Property EN 10088-1 X5CrNiMoTi15-2 ASTM A276/A276M S42010
Standard EN 10088-1:2014 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.15-0.30
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.030
Cr (%) 13.5-15.5 13.5-15.0
Mo (%) 0.20-1.20 0.40-0.85
Ni (%) 1.00-2.50 0.35-0.85
Ti (%) 0.30-0.50 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X5CrNiMoTi15-2 ASTM A276/A276M S42010
Hardness Not specified <=235 HB
Condition Not specified Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
EN 10088-1 X5CrNiMoTi15-2
Not documented
ASTM A276/A276M S42010
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can EN 10088-1 X5CrNiMoTi15-2 Be Substituted With ASTM A276/A276M S42010?
EN 10088-1 X5CrNiMoTi15-2 and ASTM A276/A276M S42010 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-1 X5CrNiMoTi15-2
0 active listings and RFQs →
ASTM A276/A276M S42010
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X5CrNiMoTi15-2 and ASTM A276/A276M S42010?
EN 10088-1 X5CrNiMoTi15-2 specifies Ti which is not specified for ASTM A276/A276M S42010.
Can EN 10088-1 X5CrNiMoTi15-2 be substituted with ASTM A276/A276M S42010?
EN 10088-1 X5CrNiMoTi15-2 and ASTM A276/A276M S42010 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.