Strong Match — 97.2% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X6Cr13 (EN 10088-1:2014) and EN 10088-2 X6CrAl13 (EN 10088-2:2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X6Cr13 is defined under European Standard (EN), originating from Europe, while EN 10088-2 X6CrAl13 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-1 X6Cr13 vs EN 10088-2 X6CrAl13 is a 97.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 97.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X6Cr13
EN 10088-2 X6CrAl13
Tensile Strength
Not specified
400-600 MPa
Condition
Not specified
Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Yield Strength
Not specified
>=230 MPa
Elongation
Not specified
>=17%
Typical Applications
EN 10088-1 X6Cr13
Not documented
EN 10088-2 X6CrAl13
General purposes, hot or cold rolled sheet/plate and strip
Key Differences
EN 10088-2 X6CrAl13 specifies Al which is not specified for EN 10088-1 X6Cr13.
Can EN 10088-1 X6Cr13 Be Substituted With EN 10088-2 X6CrAl13?
EN 10088-1 X6Cr13 and EN 10088-2 X6CrAl13 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X6CrAl13 is often considered as a substitute for EN 10088-1 X6Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X6Cr13 and EN 10088-2 X6CrAl13?
EN 10088-2 X6CrAl13 specifies Al which is not specified for EN 10088-1 X6Cr13.
Can EN 10088-1 X6Cr13 be substituted with EN 10088-2 X6CrAl13?
EN 10088-1 X6Cr13 and EN 10088-2 X6CrAl13 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X6CrAl13 is often considered as a substitute for EN 10088-1 X6Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.