EN 10088-1 X6CrNiSiNCe19-10 vs EN 10088-3 X5CrNiN19-9

Close Alternative — 81.5% match based on chemical composition and mechanical property overlap.

EN 10088-1 X6CrNiSiNCe19-10 (EN 10088-1:2014) and EN 10088-3 X5CrNiN19-9 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X6CrNiSiNCe19-10 is defined under European Standard (EN), originating from Europe, while EN 10088-3 X5CrNiN19-9 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X6CrNiSiNCe19-10 vs EN 10088-3 X5CrNiN19-9 is a 81.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.5%.

Frequently Compared With EN 10088-1 X6CrNiSiNCe19-10:
GOST 5632 08X18H10 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
81.5%
MECHANICAL MATCH
No shared data
OVERALL
81.5%
Specifications
Property EN 10088-1 X6CrNiSiNCe19-10 EN 10088-3 X5CrNiN19-9
Standard EN 10088-1:2014 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) 0.04-0.08 <=0.06
Si (%) 1.00-2.00 <=1.00
Mn (%) <=1.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 18.0-20.0 18.0-20.0
Ni (%) 9.0-11.0 8.0-11.0
N (%) 0.12-0.20 0.12-0.22
Ce (%) 0.03-0.08 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X6CrNiSiNCe19-10 EN 10088-3 X5CrNiN19-9
Tensile Strength Not specified 550-750 MPa
Yield Strength Not specified >=270 MPa
Elongation Not specified >=40%
Hardness Not specified <=215 HB
Condition Not specified Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 40 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
EN 10088-1 X6CrNiSiNCe19-10
Not documented
EN 10088-3 X5CrNiN19-9
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Key Differences
Can EN 10088-1 X6CrNiSiNCe19-10 Be Substituted With EN 10088-3 X5CrNiN19-9?
EN 10088-1 X6CrNiSiNCe19-10 and EN 10088-3 X5CrNiN19-9 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-1 X6CrNiSiNCe19-10
0 active listings and RFQs →
EN 10088-3 X5CrNiN19-9
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X6CrNiSiNCe19-10 and EN 10088-3 X5CrNiN19-9?
EN 10088-1 X6CrNiSiNCe19-10 specifies Ce which is not specified for EN 10088-3 X5CrNiN19-9.
Can EN 10088-1 X6CrNiSiNCe19-10 be substituted with EN 10088-3 X5CrNiN19-9?
EN 10088-1 X6CrNiSiNCe19-10 and EN 10088-3 X5CrNiN19-9 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.