Close Alternative — 76.2% match based on chemical composition and mechanical property overlap.

EN 10088-1 X6CrNiTi12 (EN 10088-1:2014) and JIS G4304 SUS410S (JIS G4304:2021) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X6CrNiTi12 is defined under European Standard (EN), originating from Europe, while JIS G4304 SUS410S is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, EN 10088-1 X6CrNiTi12 vs JIS G4304 SUS410S is a 76.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.2%.

Frequently Compared With EN 10088-1 X6CrNiTi12:
GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
76.2%
MECHANICAL MATCH
No shared data
OVERALL
76.2%
Specifications
Property EN 10088-1 X6CrNiTi12 JIS G4304 SUS410S
Standard EN 10088-1:2014 JIS G4304:2021
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=0.70 <=1.00
Mn (%) <=1.50 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.030
Cr (%) 10.5-12.5 11.50-13.50
Ni (%) 0.50-1.50 <=0.60
Ti (%) 0.05-0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X6CrNiTi12 JIS G4304 SUS410S
Tensile Strength Not specified >=410 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=20%
Hardness Not specified <=183 HB
Condition Not specified Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
EN 10088-1 X6CrNiTi12
Not documented
JIS G4304 SUS410S
Hot-rolled stainless steel plates and strips
Key Differences
Can EN 10088-1 X6CrNiTi12 Be Substituted With JIS G4304 SUS410S?
EN 10088-1 X6CrNiTi12 and JIS G4304 SUS410S are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-1 X6CrNiTi12
0 active listings and RFQs →
JIS G4304 SUS410S
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X6CrNiTi12 and JIS G4304 SUS410S?
EN 10088-1 X6CrNiTi12 specifies Ti which is not specified for JIS G4304 SUS410S.
Can EN 10088-1 X6CrNiTi12 be substituted with JIS G4304 SUS410S?
EN 10088-1 X6CrNiTi12 and JIS G4304 SUS410S are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.