EN 10088-1 X6NiCrNbCe32-27 vs ASTM A240/A240M S33228

Strong Match — 96.3% match based on chemical composition and mechanical property overlap.

EN 10088-1 X6NiCrNbCe32-27 (EN 10088-1:2014) and ASTM A240/A240M S33228 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X6NiCrNbCe32-27 is defined under European Standard (EN), originating from Europe, while ASTM A240/A240M S33228 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X6NiCrNbCe32-27 vs ASTM A240/A240M S33228 is a 96.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 96.3%.

Frequently Compared With EN 10088-1 X6NiCrNbCe32-27:
EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
96.3%
MECHANICAL MATCH
No shared data
OVERALL
96.3%
Specifications
Property EN 10088-1 X6NiCrNbCe32-27 ASTM A240/A240M S33228
Standard EN 10088-1:2014 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) 0.04-0.08 0.04-0.08
Si (%) <=0.30 <=0.30
Mn (%) <=1.00 <=1.00
P (%) <=0.020 <=0.020
S (%) <=0.010 <=0.015
Cr (%) 26.0-28.0 26.0-28.0
Ni (%) 31.0-33.0 31.0-33.0
N (%) <=0.10 Not specified
Al (%) <=0.025 <=0.025
Ce (%) 0.05-0.10 0.05-0.10
Nb (%) 0.60-1.00 0.6-1.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X6NiCrNbCe32-27 ASTM A240/A240M S33228
Tensile Strength Not specified >=500 MPa
Yield Strength Not specified >=185 MPa
Elongation Not specified >=30%
Hardness Not specified <=217 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
EN 10088-1 X6NiCrNbCe32-27
Not documented
ASTM A240/A240M S33228
Pressure vessels and general applications (plate, sheet and strip)
Key Differences
Can EN 10088-1 X6NiCrNbCe32-27 Be Substituted With ASTM A240/A240M S33228?
EN 10088-1 X6NiCrNbCe32-27 and ASTM A240/A240M S33228 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S33228 is often considered as a substitute for EN 10088-1 X6NiCrNbCe32-27 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X6NiCrNbCe32-27
0 active listings and RFQs →
ASTM A240/A240M S33228
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X6NiCrNbCe32-27 and ASTM A240/A240M S33228?
EN 10088-1 X6NiCrNbCe32-27 specifies N which is not specified for ASTM A240/A240M S33228.
Can EN 10088-1 X6NiCrNbCe32-27 be substituted with ASTM A240/A240M S33228?
EN 10088-1 X6NiCrNbCe32-27 and ASTM A240/A240M S33228 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S33228 is often considered as a substitute for EN 10088-1 X6NiCrNbCe32-27 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.