EN 10088-1 X8CrNiNb16-13 vs ASTM A240/A240M S30500
Close Alternative — 74.8% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X8CrNiNb16-13 (EN 10088-1:2014) and ASTM A240/A240M S30500 (ASTM A240/A240M:2025) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X8CrNiNb16-13 is defined under European Standard (EN), originating from Europe, while ASTM A240/A240M S30500 is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-1 X8CrNiNb16-13 vs ASTM A240/A240M S30500 is a 74.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 74.8%.
Frequently Compared With EN 10088-1 X8CrNiNb16-13:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X8CrNiNb16-13
ASTM A240/A240M S30500
Tensile Strength
Not specified
>=485 MPa
Yield Strength
Not specified
>=170 MPa
Elongation
Not specified
>=40%
Hardness
Not specified
<=183 HB
Condition
Not specified
Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
EN 10088-1 X8CrNiNb16-13
Not documented
ASTM A240/A240M S30500
Pressure vessels and general applications (plate, sheet and strip)
Can EN 10088-1 X8CrNiNb16-13 Be Substituted With ASTM A240/A240M S30500?
EN 10088-1 X8CrNiNb16-13 and ASTM A240/A240M S30500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-1 X8CrNiNb16-13 and ASTM A240/A240M S30500?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X8CrNiNb16-13 be substituted with ASTM A240/A240M S30500?
EN 10088-1 X8CrNiNb16-13 and ASTM A240/A240M S30500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.