EN 10088-1 X8CrNiNb16-13 vs IS 1570 (Part 7) 7Cr18Ni10H
Close Alternative — 76.6% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X8CrNiNb16-13 (EN 10088-1:2014) and IS 1570 (Part 7) 7Cr18Ni10H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X8CrNiNb16-13 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 7Cr18Ni10H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X8CrNiNb16-13 vs IS 1570 (Part 7) 7Cr18Ni10H is a 76.6% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 76.6%.
Frequently Compared With EN 10088-1 X8CrNiNb16-13:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X8CrNiNb16-13
IS 1570 (Part 7) 7Cr18Ni10H
Tensile Strength
Not specified
490-690 MPa
Yield Strength
Not specified
>=195 MPa (0.2 % proof stress)
Elongation
Not specified
>=30%
Condition
Not specified
Tubes, forgings, plates, Q, thickness - (first row of Table 3)
Typical Applications
EN 10088-1 X8CrNiNb16-13
Not documented
IS 1570 (Part 7) 7Cr18Ni10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can EN 10088-1 X8CrNiNb16-13 Be Substituted With IS 1570 (Part 7) 7Cr18Ni10H?
EN 10088-1 X8CrNiNb16-13 and IS 1570 (Part 7) 7Cr18Ni10H are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-1 X8CrNiNb16-13 and IS 1570 (Part 7) 7Cr18Ni10H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X8CrNiNb16-13 be substituted with IS 1570 (Part 7) 7Cr18Ni10H?
EN 10088-1 X8CrNiNb16-13 and IS 1570 (Part 7) 7Cr18Ni10H are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.