EN 10088-1 X10CrAlSi7 vs IS 11169 (Part 2) X04Cr17

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-1 X10CrAlSi7 (EN 10088-1:2023) and IS 11169 (Part 2) X04Cr17 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X10CrAlSi7 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X04Cr17 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X10CrAlSi7 vs IS 11169 (Part 2) X04Cr17 is a 81.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-1 X10CrAlSi7:
GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
81.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-1 X10CrAlSi7 IS 11169 (Part 2) X04Cr17
Standard EN 10088-1:2023 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.08
Si (%) 0.50-1.00 <=1.00
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.030
Cr (%) 6.0-8.0 16.0-18.0
Al (%) 0.50-1.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X10CrAlSi7 IS 11169 (Part 2) X04Cr17
Reduction of Area, soft annealed (+A) Not specified >=63% (over 5 to 25 mm)
Tensile Strength, soft annealed (+A) Not specified <=560 MPa (over 5 to 25 mm)
Typical Applications
EN 10088-1 X10CrAlSi7
Not documented
IS 11169 (Part 2) X04Cr17
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
Key Differences
Can EN 10088-1 X10CrAlSi7 Be Substituted With IS 11169 (Part 2) X04Cr17?
EN 10088-1 X10CrAlSi7 and IS 11169 (Part 2) X04Cr17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-1 X10CrAlSi7
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X10CrAlSi7 and IS 11169 (Part 2) X04Cr17?
EN 10088-1 X10CrAlSi7 specifies Al which is not specified for IS 11169 (Part 2) X04Cr17.
Can EN 10088-1 X10CrAlSi7 be substituted with IS 11169 (Part 2) X04Cr17?
EN 10088-1 X10CrAlSi7 and IS 11169 (Part 2) X04Cr17 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.