EN 10088-1 X10NiCrAlTi32-21 vs ASTM A276/A276M N08800

Strong Match — 92% match based on chemical composition and mechanical property overlap.

EN 10088-1 X10NiCrAlTi32-21 (EN 10088-1:2023) and ASTM A276/A276M N08800 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X10NiCrAlTi32-21 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M N08800 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X10NiCrAlTi32-21 vs ASTM A276/A276M N08800 is a 92% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92%.

Frequently Compared With EN 10088-1 X10NiCrAlTi32-21:
ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
92%
MECHANICAL MATCH
No shared data
OVERALL
92%
Specifications
Property EN 10088-1 X10NiCrAlTi32-21 ASTM A276/A276M N08800
Standard EN 10088-1:2023 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.10
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=1.50
P (%) <=0.030 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 19.0-23.0 19.0-23.0
Ni (%) 30.0-34.0 30.0-35.0
Al (%) 0.15-0.60 0.15-0.60
Ti (%) 0.15-0.60 0.15-0.60
Fe (%) Not specified >=39.5
Cu (%) Not specified <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X10NiCrAlTi32-21 ASTM A276/A276M N08800
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa
Elongation Not specified >=30%
Hardness Not specified <=192 HB
Condition Not specified Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
EN 10088-1 X10NiCrAlTi32-21
Not documented
ASTM A276/A276M N08800
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can EN 10088-1 X10NiCrAlTi32-21 Be Substituted With ASTM A276/A276M N08800?
EN 10088-1 X10NiCrAlTi32-21 and ASTM A276/A276M N08800 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M N08800 is often considered as a substitute for EN 10088-1 X10NiCrAlTi32-21 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X10NiCrAlTi32-21
0 active listings and RFQs →
ASTM A276/A276M N08800
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X10NiCrAlTi32-21 and ASTM A276/A276M N08800?
ASTM A276/A276M N08800 specifies Fe, Cu which are not specified for EN 10088-1 X10NiCrAlTi32-21.
Can EN 10088-1 X10NiCrAlTi32-21 be substituted with ASTM A276/A276M N08800?
EN 10088-1 X10NiCrAlTi32-21 and ASTM A276/A276M N08800 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M N08800 is often considered as a substitute for EN 10088-1 X10NiCrAlTi32-21 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.