Strong Match — 91.8% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X12Cr13 (EN 10088-1:2023) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X12Cr13 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X12Cr13 vs IS 1570 (Part 7) 12Cr13H is a 91.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 91.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X12Cr13
IS 1570 (Part 7) 12Cr13H
Tensile Strength
Not specified
470-670 MPa
Yield Strength
Not specified
>=265 MPa (0.2 % proof stress)
Elongation
Not specified
>=20%
Condition
Not specified
Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Typical Applications
EN 10088-1 X12Cr13
Not documented
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can EN 10088-1 X12Cr13 Be Substituted With IS 1570 (Part 7) 12Cr13H?
EN 10088-1 X12Cr13 and IS 1570 (Part 7) 12Cr13H overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 7) 12Cr13H is often considered as a substitute for EN 10088-1 X12Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-1 X12Cr13 and IS 1570 (Part 7) 12Cr13H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X12Cr13 be substituted with IS 1570 (Part 7) 12Cr13H?
EN 10088-1 X12Cr13 and IS 1570 (Part 7) 12Cr13H overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 7) 12Cr13H is often considered as a substitute for EN 10088-1 X12Cr13 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.