EN 10088-1 X12CrMnNiN17-7-5 vs EN 10088-3 X12CrMnNiN17-7-5

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-1 X12CrMnNiN17-7-5 (EN 10088-1:2023) and EN 10088-3 X12CrMnNiN17-7-5 (EN 10088-3:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X12CrMnNiN17-7-5 is defined under European Standard (EN), originating from Europe, while EN 10088-3 X12CrMnNiN17-7-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X12CrMnNiN17-7-5 vs EN 10088-3 X12CrMnNiN17-7-5 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-1 X12CrMnNiN17-7-5:
ASTM A959 201 EN 10088-1 1.4006 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-1 X12CrMnNiN17-7-5 EN 10088-3 X12CrMnNiN17-7-5
Standard EN 10088-1:2023 EN 10088-3:2014
Category Stainless Steel Stainless Steel
C (%) <=0.15 <=0.15
Si (%) <=1.00 <=1.00
Mn (%) 5.5-7.5 5.5-7.5
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 16.0-18.0 16.0-18.0
Ni (%) 3.5-5.5 3.5-5.5
N (%) 0.05-0.25 0.05-0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X12CrMnNiN17-7-5 EN 10088-3 X12CrMnNiN17-7-5
Tensile Strength Not specified 680-880 MPa
Yield Strength Not specified >=230 MPa
Elongation Not specified >=40%
Hardness Not specified <=260 HB
Condition Not specified Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Typical Applications
EN 10088-1 X12CrMnNiN17-7-5
Not documented
EN 10088-3 X12CrMnNiN17-7-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
Can EN 10088-1 X12CrMnNiN17-7-5 Be Substituted With EN 10088-3 X12CrMnNiN17-7-5?
EN 10088-1 X12CrMnNiN17-7-5 and EN 10088-3 X12CrMnNiN17-7-5 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X12CrMnNiN17-7-5 is often considered as a substitute for EN 10088-1 X12CrMnNiN17-7-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X12CrMnNiN17-7-5
0 active listings and RFQs →
EN 10088-3 X12CrMnNiN17-7-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X12CrMnNiN17-7-5 and EN 10088-3 X12CrMnNiN17-7-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X12CrMnNiN17-7-5 be substituted with EN 10088-3 X12CrMnNiN17-7-5?
EN 10088-1 X12CrMnNiN17-7-5 and EN 10088-3 X12CrMnNiN17-7-5 overlap closely enough on chemistry and mechanical properties that EN 10088-3 X12CrMnNiN17-7-5 is often considered as a substitute for EN 10088-1 X12CrMnNiN17-7-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.