EN 10088-1 X12CrNiWTiB16-13 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH

Close Alternative — 77.8% match based on chemical composition and mechanical property overlap.

EN 10088-1 X12CrNiWTiB16-13 (EN 10088-1:2023) and IS 1570 (Part 7) 11Cr17Ni13W3TiH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X12CrNiWTiB16-13 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 11Cr17Ni13W3TiH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X12CrNiWTiB16-13 vs IS 1570 (Part 7) 11Cr17Ni13W3TiH is a 77.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.8%.

Frequently Compared With EN 10088-1 X12CrNiWTiB16-13:
ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
77.8%
MECHANICAL MATCH
No shared data
OVERALL
77.8%
Specifications
Property EN 10088-1 X12CrNiWTiB16-13 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Standard EN 10088-1:2023 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.07-0.15 0.07-0.15
Si (%) <=0.50 <=1.00
Mn (%) <=1.50 <=1.00
P (%) <=0.035 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 15.5-17.5 15.5-17.50
Ni (%) 12.5-14.5 12.00-14.50
Ti (%) 0.40-0.70 >=4xC, <=0.80
W (%) 2.50-3.00 2.5-3.5
B (%) 0.0015-0.0060 <=0.0006
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X12CrNiWTiB16-13 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Tensile Strength Not specified 600-800 MPa
Yield Strength Not specified >=390 MPa (0.2 % proof stress)
Elongation Not specified >=25%
Condition Not specified Bars, forgings, pipes, hot cold worked, thickness up to 60 (first row of Table 3)
Typical Applications
EN 10088-1 X12CrNiWTiB16-13
Not documented
IS 1570 (Part 7) 11Cr17Ni13W3TiH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can EN 10088-1 X12CrNiWTiB16-13 Be Substituted With IS 1570 (Part 7) 11Cr17Ni13W3TiH?
EN 10088-1 X12CrNiWTiB16-13 and IS 1570 (Part 7) 11Cr17Ni13W3TiH are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-1 X12CrNiWTiB16-13
0 active listings and RFQs →
IS 1570 (Part 7) 11Cr17Ni13W3TiH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X12CrNiWTiB16-13 and IS 1570 (Part 7) 11Cr17Ni13W3TiH?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X12CrNiWTiB16-13 be substituted with IS 1570 (Part 7) 11Cr17Ni13W3TiH?
EN 10088-1 X12CrNiWTiB16-13 and IS 1570 (Part 7) 11Cr17Ni13W3TiH are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.