EN 10088-1 X1CrNiMoCu12-5-2 vs EN 10088-2 X1CrNiMoCu12-5-2

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-1 X1CrNiMoCu12-5-2 (EN 10088-1:2023) and EN 10088-2 X1CrNiMoCu12-5-2 (EN 10088-2:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X1CrNiMoCu12-5-2 is defined under European Standard (EN), originating from Europe, while EN 10088-2 X1CrNiMoCu12-5-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X1CrNiMoCu12-5-2 vs EN 10088-2 X1CrNiMoCu12-5-2 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-1 X1CrNiMoCu12-5-2:
ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-1 X1CrNiMoCu12-5-2 EN 10088-2 X1CrNiMoCu12-5-2
Standard EN 10088-1:2023 EN 10088-2:2014
Category Stainless Steel Stainless Steel
C (%) <=0.020 <=0.020
Si (%) <=0.50 <=0.50
Mn (%) <=2.00 <=2.00
P (%) <=0.040 <=0.040
S (%) <=0.003 <=0.003
Cr (%) 11.0-13.0 11.0-13.0
Mo (%) 1.30-1.80 1.30-1.80
Ni (%) 4.0-5.0 4.0-5.0
Cu (%) 0.20-0.80 0.20-0.80
N (%) <=0.020 <=0.020
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X1CrNiMoCu12-5-2 EN 10088-2 X1CrNiMoCu12-5-2
Tensile Strength Not specified 750-950 MPa
Yield Strength Not specified >=550 MPa
Elongation Not specified >=15%
Hardness Not specified <=300 HB
Condition Not specified Annealed (+A), hot rolled strip, up to 13.5 mm thick
Typical Applications
EN 10088-1 X1CrNiMoCu12-5-2
Not documented
EN 10088-2 X1CrNiMoCu12-5-2
General purposes, hot or cold rolled sheet/plate and strip
Can EN 10088-1 X1CrNiMoCu12-5-2 Be Substituted With EN 10088-2 X1CrNiMoCu12-5-2?
EN 10088-1 X1CrNiMoCu12-5-2 and EN 10088-2 X1CrNiMoCu12-5-2 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X1CrNiMoCu12-5-2 is often considered as a substitute for EN 10088-1 X1CrNiMoCu12-5-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X1CrNiMoCu12-5-2
0 active listings and RFQs →
EN 10088-2 X1CrNiMoCu12-5-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X1CrNiMoCu12-5-2 and EN 10088-2 X1CrNiMoCu12-5-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X1CrNiMoCu12-5-2 be substituted with EN 10088-2 X1CrNiMoCu12-5-2?
EN 10088-1 X1CrNiMoCu12-5-2 and EN 10088-2 X1CrNiMoCu12-5-2 overlap closely enough on chemistry and mechanical properties that EN 10088-2 X1CrNiMoCu12-5-2 is often considered as a substitute for EN 10088-1 X1CrNiMoCu12-5-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.