Close Alternative — 82.1% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X1NiCrMoCu25-20-5 (EN 10088-1:2023) and JIS G4304 SUS890L (JIS G4304:2021) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X1NiCrMoCu25-20-5 is defined under European Standard (EN), originating from Europe, while JIS G4304 SUS890L is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, EN 10088-1 X1NiCrMoCu25-20-5 vs JIS G4304 SUS890L is a 82.1% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 82.1%.
Frequently Compared With EN 10088-1 X1NiCrMoCu25-20-5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X1NiCrMoCu25-20-5
JIS G4304 SUS890L
Tensile Strength
Not specified
>=490 MPa
Yield Strength
Not specified
>=215 MPa
Elongation
Not specified
>=35%
Hardness
Not specified
<=187 HB
Condition
Not specified
Solution heat treated plate and strip; 0.2 percent proof strength applies only when specified by the purchaser
Typical Applications
EN 10088-1 X1NiCrMoCu25-20-5
Not documented
JIS G4304 SUS890L
Hot-rolled stainless steel plates and strips
Key Differences
EN 10088-1 X1NiCrMoCu25-20-5 specifies N which is not specified for JIS G4304 SUS890L.
Can EN 10088-1 X1NiCrMoCu25-20-5 Be Substituted With JIS G4304 SUS890L?
EN 10088-1 X1NiCrMoCu25-20-5 and JIS G4304 SUS890L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-1 X1NiCrMoCu25-20-5 and JIS G4304 SUS890L?
EN 10088-1 X1NiCrMoCu25-20-5 specifies N which is not specified for JIS G4304 SUS890L.
Can EN 10088-1 X1NiCrMoCu25-20-5 be substituted with JIS G4304 SUS890L?
EN 10088-1 X1NiCrMoCu25-20-5 and JIS G4304 SUS890L are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.