Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X25CrMnNiN25-9-7 (EN 10088-1:2023) and ASTM A959 310H (ASTM A959:2011) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X25CrMnNiN25-9-7 is defined under European Standard (EN), originating from Europe, while ASTM A959 310H is defined under ASTM International, originating from United States.
As per chemical composition, EN 10088-1 X25CrMnNiN25-9-7 vs ASTM A959 310H is a 70.8% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Frequently Compared With EN 10088-1 X25CrMnNiN25-9-7:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Typical Applications
EN 10088-1 X25CrMnNiN25-9-7
Not documented
ASTM A959 310H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
EN 10088-1 X25CrMnNiN25-9-7 specifies N which is not specified for ASTM A959 310H.
Can EN 10088-1 X25CrMnNiN25-9-7 Be Substituted With ASTM A959 310H?
EN 10088-1 X25CrMnNiN25-9-7 and ASTM A959 310H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 X25CrMnNiN25-9-7 and ASTM A959 310H?
EN 10088-1 X25CrMnNiN25-9-7 specifies N which is not specified for ASTM A959 310H.
Can EN 10088-1 X25CrMnNiN25-9-7 be substituted with ASTM A959 310H?
EN 10088-1 X25CrMnNiN25-9-7 and ASTM A959 310H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.