Close Alternative — 83.5% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X2CrCuNiN23-2-2 (EN 10088-1:2023) and IS 6603 X02Cr22Ni2N (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X2CrCuNiN23-2-2 is defined under European Standard (EN), originating from Europe, while IS 6603 X02Cr22Ni2N is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X2CrCuNiN23-2-2 vs IS 6603 X02Cr22Ni2N is a 83.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 83.5%.
Frequently Compared With EN 10088-1 X2CrCuNiN23-2-2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X2CrCuNiN23-2-2
IS 6603 X02Cr22Ni2N
Tensile Strength
Not specified
>=650 MPa
Yield Strength
Not specified
>=380 MPa
Elongation
Not specified
>=30%
Hardness
Not specified
<=290 HB
Condition
Not specified
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Tensile Strength is a minimum as printed, hardness for guidance only
Typical Applications
EN 10088-1 X2CrCuNiN23-2-2
Not documented
IS 6603 X02Cr22Ni2N
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
EN 10088-1 X2CrCuNiN23-2-2 specifies Cu which is not specified for IS 6603 X02Cr22Ni2N.
Can EN 10088-1 X2CrCuNiN23-2-2 Be Substituted With IS 6603 X02Cr22Ni2N?
EN 10088-1 X2CrCuNiN23-2-2 and IS 6603 X02Cr22Ni2N are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-1 X2CrCuNiN23-2-2 and IS 6603 X02Cr22Ni2N?
EN 10088-1 X2CrCuNiN23-2-2 specifies Cu which is not specified for IS 6603 X02Cr22Ni2N.
Can EN 10088-1 X2CrCuNiN23-2-2 be substituted with IS 6603 X02Cr22Ni2N?
EN 10088-1 X2CrCuNiN23-2-2 and IS 6603 X02Cr22Ni2N are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.