EN 10088-1 X2CrNi18-9 vs IS 1570 (Part 5) X02Cr19Ni10

Strong Match — 91% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrNi18-9 (EN 10088-1:2023) and IS 1570 (Part 5) X02Cr19Ni10 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrNi18-9 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 5) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X2CrNi18-9 vs IS 1570 (Part 5) X02Cr19Ni10 is a 91% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91%.

Frequently Compared With EN 10088-1 X2CrNi18-9:
EN 10088-1 1.4301 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
91%
MECHANICAL MATCH
No shared data
OVERALL
91%
Specifications
Property EN 10088-1 X2CrNi18-9 IS 1570 (Part 5) X02Cr19Ni10
Standard EN 10088-1:2023 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.0
Mn (%) <=2.00 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 17.5-19.5 17.5-20.0
Ni (%) 8.0-10.5 8.0-12.0
N (%) <=0.10 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrNi18-9 IS 1570 (Part 5) X02Cr19Ni10
Tensile Strength Not specified >=485 MPa
Yield Strength Not specified >=170 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=183 HB; <=88 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Key Differences
Can EN 10088-1 X2CrNi18-9 Be Substituted With IS 1570 (Part 5) X02Cr19Ni10?
EN 10088-1 X2CrNi18-9 and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for EN 10088-1 X2CrNi18-9 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrNi18-9
0 active listings and RFQs →
IS 1570 (Part 5) X02Cr19Ni10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrNi18-9 and IS 1570 (Part 5) X02Cr19Ni10?
EN 10088-1 X2CrNi18-9 specifies N which is not specified for IS 1570 (Part 5) X02Cr19Ni10.
Can EN 10088-1 X2CrNi18-9 be substituted with IS 1570 (Part 5) X02Cr19Ni10?
EN 10088-1 X2CrNi18-9 and IS 1570 (Part 5) X02Cr19Ni10 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X02Cr19Ni10 is often considered as a substitute for EN 10088-1 X2CrNi18-9 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.