EN 10088-1 X2CrNiMoCuN25-6-3 vs ASTM A240/A240M S32520

Strong Match — 92.3% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrNiMoCuN25-6-3 (EN 10088-1:2023) and ASTM A240/A240M S32520 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrNiMoCuN25-6-3 is defined under European Standard (EN), originating from Europe, while ASTM A240/A240M S32520 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X2CrNiMoCuN25-6-3 vs ASTM A240/A240M S32520 is a 92.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.3%.

Frequently Compared With EN 10088-1 X2CrNiMoCuN25-6-3:
EN 10088-1 1.4845 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
92.3%
MECHANICAL MATCH
No shared data
OVERALL
92.3%
Specifications
Property EN 10088-1 X2CrNiMoCuN25-6-3 ASTM A240/A240M S32520
Standard EN 10088-1:2023 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.70 <=0.80
Mn (%) <=2.00 <=1.50
P (%) <=0.035 <=0.035
S (%) <=0.015 <=0.020
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 3.00-4.0 3.0-4.0
Ni (%) 6.0-8.0 5.5-8.0
N (%) 0.20-0.30 0.20-0.35
Cu (%) 1.00-2.50 0.50-2.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrNiMoCuN25-6-3 ASTM A240/A240M S32520
Tensile Strength Not specified >=770 MPa
Yield Strength Not specified >=550 MPa
Elongation Not specified >=25%
Hardness Not specified <=310 HB
Condition Not specified Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
EN 10088-1 X2CrNiMoCuN25-6-3
Not documented
ASTM A240/A240M S32520
Pressure vessels and general applications (plate, sheet and strip)
Can EN 10088-1 X2CrNiMoCuN25-6-3 Be Substituted With ASTM A240/A240M S32520?
EN 10088-1 X2CrNiMoCuN25-6-3 and ASTM A240/A240M S32520 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S32520 is often considered as a substitute for EN 10088-1 X2CrNiMoCuN25-6-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrNiMoCuN25-6-3
0 active listings and RFQs →
ASTM A240/A240M S32520
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrNiMoCuN25-6-3 and ASTM A240/A240M S32520?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X2CrNiMoCuN25-6-3 be substituted with ASTM A240/A240M S32520?
EN 10088-1 X2CrNiMoCuN25-6-3 and ASTM A240/A240M S32520 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S32520 is often considered as a substitute for EN 10088-1 X2CrNiMoCuN25-6-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.