EN 10088-1 X2CrNiMoN17-13-3 vs IS 11169 (Part 2) X02Cr17Ni12Mo3N

Strong Match — 93.8% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrNiMoN17-13-3 (EN 10088-1:2023) and IS 11169 (Part 2) X02Cr17Ni12Mo3N (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrNiMoN17-13-3 is defined under European Standard (EN), originating from Europe, while IS 11169 (Part 2) X02Cr17Ni12Mo3N is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-1 X2CrNiMoN17-13-3 vs IS 11169 (Part 2) X02Cr17Ni12Mo3N is a 93.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.8%.

Frequently Compared With EN 10088-1 X2CrNiMoN17-13-3:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
93.8%
MECHANICAL MATCH
No shared data
OVERALL
93.8%
Specifications
Property EN 10088-1 X2CrNiMoN17-13-3 IS 11169 (Part 2) X02Cr17Ni12Mo3N
Standard EN 10088-1:2023 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 16.5-18.5 16.5-18.5
Mo (%) 2.50-3.00 2.50-3.00
Ni (%) 11.0-14.0 10.5-13.0
N (%) 0.12-0.22 0.12-0.22
Cu (%) Not specified <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrNiMoN17-13-3 IS 11169 (Part 2) X02Cr17Ni12Mo3N
Reduction of Area, solution annealed (+AT) Not specified >=60% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) Not specified <=780 MPa (over 5 to 50 mm)
Typical Applications
EN 10088-1 X2CrNiMoN17-13-3
Not documented
IS 11169 (Part 2) X02Cr17Ni12Mo3N
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Key Differences
Can EN 10088-1 X2CrNiMoN17-13-3 Be Substituted With IS 11169 (Part 2) X02Cr17Ni12Mo3N?
EN 10088-1 X2CrNiMoN17-13-3 and IS 11169 (Part 2) X02Cr17Ni12Mo3N overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr17Ni12Mo3N is often considered as a substitute for EN 10088-1 X2CrNiMoN17-13-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrNiMoN17-13-3
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr17Ni12Mo3N
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrNiMoN17-13-3 and IS 11169 (Part 2) X02Cr17Ni12Mo3N?
IS 11169 (Part 2) X02Cr17Ni12Mo3N specifies Cu which is not specified for EN 10088-1 X2CrNiMoN17-13-3.
Can EN 10088-1 X2CrNiMoN17-13-3 be substituted with IS 11169 (Part 2) X02Cr17Ni12Mo3N?
EN 10088-1 X2CrNiMoN17-13-3 and IS 11169 (Part 2) X02Cr17Ni12Mo3N overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr17Ni12Mo3N is often considered as a substitute for EN 10088-1 X2CrNiMoN17-13-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.