EN 10088-1 X2CrNiMoSi18-5-3 vs IS 6603 X02Cr18Ni14Mo3
Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X2CrNiMoSi18-5-3 (EN 10088-1:2023) and IS 6603 X02Cr18Ni14Mo3 (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X2CrNiMoSi18-5-3 is defined under European Standard (EN), originating from Europe, while IS 6603 X02Cr18Ni14Mo3 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X2CrNiMoSi18-5-3 vs IS 6603 X02Cr18Ni14Mo3 is a 75.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Frequently Compared With EN 10088-1 X2CrNiMoSi18-5-3:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X2CrNiMoSi18-5-3
IS 6603 X02Cr18Ni14Mo3
Tensile Strength
Not specified
500-700 MPa
Yield Strength
Not specified
>=200 MPa
Elongation
Not specified
>=40%
Condition
Not specified
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-1 X2CrNiMoSi18-5-3
Not documented
IS 6603 X02Cr18Ni14Mo3
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-1 X2CrNiMoSi18-5-3 Be Substituted With IS 6603 X02Cr18Ni14Mo3?
EN 10088-1 X2CrNiMoSi18-5-3 and IS 6603 X02Cr18Ni14Mo3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 X2CrNiMoSi18-5-3 and IS 6603 X02Cr18Ni14Mo3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 X2CrNiMoSi18-5-3 be substituted with IS 6603 X02Cr18Ni14Mo3?
EN 10088-1 X2CrNiMoSi18-5-3 and IS 6603 X02Cr18Ni14Mo3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.