EN 10088-1 X2NiCrAlTi32-20 vs IS 1570 (Part 7) 3Cr18Ni11H
Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-1 X2NiCrAlTi32-20 (EN 10088-1:2023) and IS 1570 (Part 7) 3Cr18Ni11H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 X2NiCrAlTi32-20 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 3Cr18Ni11H is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 X2NiCrAlTi32-20 vs IS 1570 (Part 7) 3Cr18Ni11H is a 73.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Frequently Compared With EN 10088-1 X2NiCrAlTi32-20:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 X2NiCrAlTi32-20
IS 1570 (Part 7) 3Cr18Ni11H
Tensile Strength
Not specified
490-690 MPa
Yield Strength
Not specified
>=175 MPa (0.2 % proof stress)
Elongation
Not specified
>=30%
Condition
Not specified
Tubes, forgings, plates, Q, thickness - (first row of Table 3)
Typical Applications
EN 10088-1 X2NiCrAlTi32-20
Not documented
IS 1570 (Part 7) 3Cr18Ni11H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
EN 10088-1 X2NiCrAlTi32-20 specifies Al which is not specified for IS 1570 (Part 7) 3Cr18Ni11H.
Can EN 10088-1 X2NiCrAlTi32-20 Be Substituted With IS 1570 (Part 7) 3Cr18Ni11H?
EN 10088-1 X2NiCrAlTi32-20 and IS 1570 (Part 7) 3Cr18Ni11H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 X2NiCrAlTi32-20 and IS 1570 (Part 7) 3Cr18Ni11H?
EN 10088-1 X2NiCrAlTi32-20 specifies Al which is not specified for IS 1570 (Part 7) 3Cr18Ni11H.
Can EN 10088-1 X2NiCrAlTi32-20 be substituted with IS 1570 (Part 7) 3Cr18Ni11H?
EN 10088-1 X2NiCrAlTi32-20 and IS 1570 (Part 7) 3Cr18Ni11H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.